Effect of LED curing on microleakage and microhardness of Class V resin-based composite restorations

No Thumbnail Available
File version
Author(s)
Oberholzer, Theunis
Schunemann, Marita
Kidd, Martin
Griffith University Author(s)
Primary Supervisor
Other Supervisors
Editor(s)
Date
2004
Size
File type(s)
Location
License
Abstract

Background: Polymerisation shrinkage is a critical limitation of dental composites and may contribute to microleakage, postoperative pain, tooth fracture, and secondary caries. It has been shown that curing methods play asignificant role in polymerisation shrinkage of light-cured dental resins. The purpose of this study was to investigate the effect of a LED curing light on microleakage as well as microhardness of a dental composite. Method: For the microleakage test 32 Class V cavities were prepared in human premolars, conditioned with 35% phosphoric acid and treated with the bonding agent Prime & Bond NT. They were then incrementally filled with the composite Esthet-X and randomly divided into two groups of 16 each. The first group was cured by means of a Spectrum 800 set at 500mW/cm2 for 40 seconds and the second group with the GC E-Light in standard mode. The specimens were thermo-cycled in a 0.5% basic fuchsin solution, sectioned and evaluated for dye penetration. For the microhardness test two groups of 6 specimens each were exposed using either the LED- or the Halogen curing unit. Vickers microhardness tests were performed immediately after curing as well as 24 hours later, on the top, and at the bottom surface. Results: At the dentine/cementum interface, significantly less microleakage (p=0.004) was found when the restorations were cured with the LED-unit. At the enamel interface no significant difference (p=0.340) in microleakage was found between curing methods. Immediately after exposure significantly harder surfaces were found at the top (p<0.001) as well as at the bottom (p<0.001), using the halogen unit (p<0.05). Conclusion: Although a reduction in microleakage could be demonstrated exposing the composite restoration to an LED LCU, an effective microhardness ratio was not achieved.

Journal Title

International Dental Journal

Conference Title
Book Title
Edition
Volume

54

Issue

1

Thesis Type
Degree Program
School
DOI
Patent number
Funder(s)
Grant identifier(s)
Rights Statement
Rights Statement
Item Access Status
Note
Access the data
Related item(s)
Subject

Dentistry not elsewhere classified

Dentistry

Persistent link to this record
Citation
Collections