KH2PO4-Assisted Synthesis and Electrochemical Performance of Highly Uniform CuBi2O4 Microspheres Hierarchically Self-Assembled by Nanoparticles

No Thumbnail Available
File version
Author(s)
Wang, Fei
Yang, Hua
Zhang, Yunchuan
Zhang, Haimin
Griffith University Author(s)
Primary Supervisor
Other Supervisors
Editor(s)
Date
2017
Size
File type(s)
Location
License
Abstract

The effect of KH2PO4 on the synthesis of CuBi2O4 microstructures was investigated. The samples were characterized by powder x-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET) analysis, x-ray photoelectron spectroscopy (XPS) and ultraviolet (UV)-visible diffuse reflectance spectroscopy. It is demonstrated that the use of KH2PO4 leads to the production of highly uniform CuBi2O4 microspheres hierarchically self-assembled by nanoparticles. With increasing the KH2PO4 concentration from 0.5 M to 1.4 M, the average diameter of the resultant microspheres decreases gradually from 3.3 μm to 1.4 μm. However, further increase in the KH2PO4 concentration up to 1.5 M leads to a sudden increase in the average diameter of the resultant microspheres up to 2.3 μm. In addition, a minor amount of bamboo leaf- or pine needle-like structures are visible in the samples prepared at the KH2PO4 concentrations of 1.0–1.5 M. The bandgap energy of the as-prepared samples is measured to be 1.89 eV by UV-visible diffuse reflectance spectroscopy. The electrochemical performance of the samples was investigated by cyclic voltammetry, galvanostatic charge-discharge measurements, and electrochemical impedance spectroscopy in 2 M KOH electrolyte. Among the hierarchical microspheres, those prepared at the KH2PO4 concentration of 1.4 M deliver a relatively higher specific capacitance due to their smaller size (1284 F g−1 at a current density of 2 A g−1).

Journal Title

Journal of Electronic Materials

Conference Title
Book Title
Edition
Volume

46

Issue

8

Thesis Type
Degree Program
School
Publisher link
Patent number
Funder(s)
Grant identifier(s)
Rights Statement
Rights Statement
Item Access Status
Note
Access the data
Related item(s)
Subject

Atomic, molecular and optical physics

Particle and high energy physics

Persistent link to this record
Citation

Wang, F; Yang, H; Zhang, Y; Zhang, H, KH2PO4-Assisted Synthesis and Electrochemical Performance of Highly Uniform CuBi2O4 Microspheres Hierarchically Self-Assembled by Nanoparticles Journal of Electronic Materials, 2017, 46 (8), pp. 4774-4783

Collections