Enhanced hydrogen desorption from Mg(BH4)2 by combining nanoconfinement and a Ni catalyst

No Thumbnail Available
File version
Author(s)
Wahab, M Abdul
Jia, Yi Alec
Yang, Dongjiang
Zhao, Huijun
Yao, Xiangdong
Griffith University Author(s)
Primary Supervisor
Other Supervisors
Editor(s)
Date
2013
Size
File type(s)
Location
License
Abstract

Magnesium borohydride (Mg(BH4)(2)) has been infiltrated into highly ordered mesoporous carbon (CMK3) containing dispersed Ni nanoparticles (Ni NPs) to investigate the possible synergetic effects of nanoconfinement and catalysis by Ni NPs. Ni NPs (5 wt%) were introduced into the CMK3 nanoscaffold (CMK3-Ni) then Mg(BH4)(2) was slowly infiltrated into this prepared CMK3-Ni template to synthesize a CMK3-Ni confined (Mg(BH4)(2)) system (denoted as CMK3-Ni-Mg(BH4)(2)). Solid-state B-11 NMR and FT-IR spectra confirmed that Mg(BH4)(2) was in the pores of CMK3-Ni. Temperature-programmed desorption-mass spectroscopy (TPD-MS) and pressure-composition-temperature (PCT) measurements were utilized to study the hydrogen desorption properties for this nanoconfined CMK3-Ni-Mg(BH4)(2) system, which was demonstrated to be remarkably improved, e. g. the hydrogen desorption temperature was dramatically decreased and the release rate was significantly enhanced. The hydrogen started to be released from the CMK3-Ni-Mg(BH4)(2) at a temperature of only 75 degrees C (measured by TPD) and reached its peak release rate at a temperature of 155 degrees C, compared with 270 degrees C and above 350 degrees C respectively from pure Mg(BH4)(2). To the best of our knowledge, this is the first time Mg(BH4)(2) decomposition has been realized at a temperature below 100 degrees C, which is of great significance for the use of this material for practical hydrogen storage for proton exchange membrane fuel cells (PEMFCs).

Journal Title

Journal of Materials Chemistry A

Conference Title
Book Title
Edition
Volume

1

Issue

10

Thesis Type
Degree Program
School
Publisher link
Patent number
Funder(s)
Grant identifier(s)
Rights Statement
Rights Statement
Item Access Status
Note
Access the data
Related item(s)
Subject

Macromolecular and materials chemistry

Materials engineering

Chemical engineering

Persistent link to this record
Citation
Collections